中文摘要: 本论文研究了低品位氧化锌矿在NH3-(NH4)2SO4-H2O体系中的浸出,并利用超声波进行了浸出过程的强化。结果表明,超声波能够强化低品位氧化锌矿在氨性浸出剂中的浸出。在总氨浓度为7.5mol/L, n[NH4 ]:n[NH3]为2:1,反应温度为40℃,反应时间为60min,超声波浸出,液固比为5:1的条件下,锌的浸出率可以达到92.1%。当NH3与(NH4)2SO4的摩尔比为1:1时,此低品位氧化锌矿在浸出Zn2 所形成的配位化合物为[Zn(NH3)4]2 。适当增加氨浓度及反应温度可有效提高锌的浸出率。
Abstract:In this paper, a process of leaching low grade zinc oxide ore leached in a NH3-(NH4)2SO4-H2O system strengthening by ultrasonic wave is present. The results demonstrated that ultrasonic wave can improve the leaching of low grade zinc oxide ore in ammonia solution. And under conditions of ultrasonic wave assisted leaching, total ammonia concentrations being 7.5mol/L, molar ratio of NH4 and NH3 being 2:1, leaching temperature 40 ℃, leaching 60 mins, and molar ratio of liquid and solid being 5:1, leaching of zinc can reach 92.1. This low grade zinc oxide ore will chelate with ammonia forming [Zn(NH3)4]2 in the leaching process, when molar ratio of NH3 and (NH4)2SO4 being 1:1. Appropriate increasing of ammonia concentration and reaction temperature can effectively improve leaching of zinc
文章编号：20170412002 中图分类号： 文献标志码：
基金项目:云南省教育厅科学研究基金资助性项目
| 作者 | 单位 | |
| 朱兴彩* | 云南锡业职业技术学院 | 792529274@qq.com |
| 杨坤 | 昆明理工大学 冶金与能源工程学院 |
引用文本：
朱兴彩,杨坤.超声波强化低品位氧化锌矿在NH3-(NH4)2SO4-H2O体系中的浸出[J].矿冶,2018,27(1):37~40.
朱兴彩,杨坤.超声波强化低品位氧化锌矿在NH3-(NH4)2SO4-H2O体系中的浸出[J].矿冶,2018,27(1):37~40.
关注微信公众号