喷雾干燥法制备包覆团聚硼粉研究
(北京矿冶研究总院,北京 100044)
RESEARCH ON THE COATED AND AGGLOMERATED BORON POWDER BY SPRAY DRYING METHOD
(Beijing General Research Institute of Mining and Metallurgy,Beijing 100044,China)
摘要
图/表
参考文献
相似文献
本文已被:浏览 3335次   下载 73
投稿时间:2010-11-10    
中文摘要: 以95级无定形硼粉为原材料,采用喷雾干燥法制备包覆团聚硼粉。考察了不同工艺参数、不同偶联剂对包覆团聚效果影响,并对团聚后的硼粉进行性能表征。理论分析和实验结果表明,采用偶联剂可有效提高团聚颗粒机械强度,并且A1偶联剂为料浆体系适合采用的偶联剂;通过控制喷雾参数可有效控制团聚颗粒形貌和粒度,并且回收率高,适合批量化生产,制备的包覆团聚硼粉球形度高,流动性能好,比表面积明显降低。
中文关键词: 含硼推进剂  硼粉  团聚  喷雾干燥
Abstract:Amorphous boron powder of 95 percent was coated and agglomerated by spray drying method. And the effects of different process parameters and different coupling agent on the agglomeration and coat were studied.It was found that coupling agent can effectively improve the mechanical strength of agglomerate particles, especially the A1 coupling agent is suitable for the slurry system. The results showed that the method can effectively control the particle morphology and size aggregates by controlling of spray parameters with a high recovery rate and it is suitable for mass production. The coated and agglomerated boron powder has appropriate solvent, good flow properties and lower surface area.
文章编号:20110211     中图分类号:    文献标志码:
基金项目:
引用文本:
张春鸣,曾克里,张 鑫,任先京.喷雾干燥法制备包覆团聚硼粉研究[J].矿冶,2011,20(2):44~48.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号