低品位氧化铜钴矿直接还原浸出工艺研究
李强
(北京矿冶科技集团有限公司)
Study on Direct Reduced Leaching of Low Grade Oxidized Copper and Cobalt Ores
Li Qiang
(BGRIMM Technology Group)
摘要
图/表
参考文献
相似文献
本文已被:浏览 278次   下载 281
投稿时间:2018-10-17    修订日期:2019-04-18
中文摘要: 针对复杂低品位氧化铜钴矿开展直接还原浸出工艺研究。结果表明,在磨矿粒度-74μm占比80~85%、液固比2/1(mL/g)、浸出温度80℃、酸耗为100kg/t矿、浸出时间4h、通SO2气体控制浸出终点电位340~350mV的条件下,Cu、Ni、Co浸出率分别为37.605%、51.184%和80.832%。在此基础上采用两段逆流浸出,可有效节约还原剂SO2的用量和实现浸出液游离酸的综合利用,节省后续中和环节碱的消耗量。
中文关键词: 氧化铜钴矿  SO2  还原浸出  两段逆流
Abstract:The direct reduced leaching of complex low grade of oxidized copper and cobalt ores was studied.The results show that the leaching rates of copper, nickel and cobalt are 37.605%、51.184% and 80.832% respectively, in the following conditions: the liquid to solid ratio 2:1,the leaching temperature 80℃, the sulfuric acid consumption 100kg/t ore, the leaching time 4 h,the ending potential 340~350mV.On this basis, the use of two stage countercurrent leaching, can effectively save the amount of reducing agent SO<sub>2</sub> and the comprehensive utilization of free acid in the leaching solution, save the alkali consumption of the following process.
文章编号:     中图分类号:    文献标志码:
基金项目:国家科技支撑计划(2013BAE04B00);
Author NameAffiliationE-mail
Li Qiang BGRIMM Technology Group lq-1@163.com 
引用文本:
李强.低品位氧化铜钴矿直接还原浸出工艺研究[J].矿冶,2019,28(3):.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号