高硅低铁锌焙砂中性浸出-液固分离试验研究
树辰
(北京矿冶科技集团有限公司)
Experimental Study on leaching and liquid-solid separation in the leaching process of high-silicon, low-iron zinc calcine
(北京矿冶科技集团有限公司)
摘要
图/表
参考文献
相似文献
本文已被:浏览 47次   下载 13
投稿时间:2019-12-07    修订日期:2020-02-17
中文摘要: 本文针对新疆某高硅、低铁锌焙砂进行中性浸出-液固分离试验研究,详细研究了浸出时间、浸出液固比、浸出温度和始酸浓度对焙砂浸出和矿浆絮凝沉降的影响,同时也进行了不同矿浆浓度絮凝沉降试验,获得了最佳中性浸出和矿浆絮凝沉降工艺参数,为生产应用提供了技术支撑。
Abstract:In this paper, the leaching test of a high-silicon, low-iron zinc calcine and the liquid-solid separation test of slurry was carried out.The effects of leaching time, leaching solid ratio, leaching temperature and initial acid concentration on the leaching and settling were studied in detail.At the same time, the flocculation and settling test of different slurry concentrations was also carried out.At last, the optimal parameters were obtained, and it has also provided technical guidance for the industrial application.
文章编号:     中图分类号:    文献标志码:
基金项目:国家自然科学基金(51434001)资助;国家重点研发计划(2018YFC1900400)资助;青年创新基金(QCJ201823)资助;国际合作项目KY201502004(科技部科技伙伴计划资助)。
引用文本:
树辰.高硅低铁锌焙砂中性浸出-液固分离试验研究[J].矿冶,2020,(4):.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号