富氧焙烧对高铜低硫精矿浸出率和脱硫率的影响
周克荣, 张汉彪, 季尚军
(华刚矿业股份有限公司)
Effect of oxygen enriched roasting on leaching rate and desulfurization rate of high copper and low sulfur concentrate
ZHOU Kerong, ZHANG hanbiao, JI Shangjun
(1 La Sino-Congolaise Des Mines S.A.)
摘要
图/表
参考文献
相似文献
本文已被:浏览 39次   下载 10
投稿时间:2019-12-30    修订日期:2020-02-05
中文摘要: 针对高铜低硫精矿的特点,采用了富氧焙烧的技术。通过进行条件实验研究得到,当焙烧时间为8 h,焙烧温度为750 ℃,焙烧富氧浓度为30 %时,焙烧效果最好,在该条件下脱硫率为70 %,焙砂浸出率为97.5 %。通过实验对比富氧焙烧与非富氧焙烧可以得出,采用富氧焙烧可以有效的缩短焙烧时间,降低焙烧所用温度,大大提高了焙烧效率。通过进行重复性验证和工业扩大化研究得出在该最佳条件具有良好的重复性,对实际生产具有一定的指导意义。
Abstract:According to the characteristics of high copper and low sulfur concentrate, oxygen enriched roasting technology is adopted. The results show that when the roasting time is 8 hours, the roasting temperature is 750 ℃, and the concentration of oxygen enrichment is 30%, the roasting effect is the best. Under this condition, the desulfurization rate is 70%, and the leaching rate of calcine is 97.5%. By comparing oxygen enriched roasting with non oxygen enriched roasting, it can be concluded that oxygen enriched roasting can effectively shorten the roasting time, reduce the temperature used in the roasting, and greatly improve the roasting efficiency. Through the research of repeatability verification and industrial expansion, it is concluded that the best condition has good repeatability, which has certain guiding significance for the actual production.
文章编号:     中图分类号:    文献标志码:
基金项目:
引用文本:
周克荣,张汉彪,季尚军.富氧焙烧对高铜低硫精矿浸出率和脱硫率的影响[J].矿冶,2020,(4):.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号