锡渣还原氯化焙烧--磁选回收有价金属试验
翟忠标1, 牟兴兵1, 陈景2
(1.昆明冶金研究院有限公司;2.昆明理工大学冶金与能源工程学院)
Experiment on Recovery of Metals from Tin Slag by Reducing Chloride Roasting and Magnetic Separation
zhaizhongbiao1, Mou Xinbing1, Chen Jing2
(1.Kunming Metallurgical Research Intitute Co., Ltd;2.Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology)
摘要
图/表
参考文献
相似文献
本文已被:浏览 47次   下载 12
投稿时间:2020-01-02    修订日期:2020-01-22
中文摘要: 对某锡渣进行还原氯化焙烧--磁选回收有价金属试验。结果表明:还原氯化焙烧的最佳条件为:焙烧温度为1000oC,焙烧时间为50min,还原剂用量为锡渣质量的20%,氯化钙用量为锡渣质量的10%,在此试验条件下,铁的磁化率为81.98%,铅的挥发率为98.88%,锌的挥发率为80.90%,锡的挥发率为96.73%。熟料磨矿细度为-75μm占95%,磁选磁场强度为0.2T,可得铁的品位为68.18%,回收率为72.03%的铁精矿。
中文关键词: 还原氯化焙烧  磁选  锡渣  氯化钙
Abstract:The experiment of recycling valuable metals from tin slag by reductive chloride roasting and magnetic separation was carried out. The results showed that while the temperature is 1000 oC, time is 50 min, reductant dosage is 20%, calcium chloride dosage is 10%. Under the optimum conditions, the magnetic susceptibility of iron is 81.98%, the volatilization rate of lead is 98.88%, the volatilization rate of zinc is 80.90%, and the volatilization rate of tin is 96.73%. When the grinding fineness of product is -75 μm accounted for 100%, the magnetic field intensity is 0.2T, the iron concentrate with Fe grade of 68.18% and recovery of 72.03% can be obtained.
文章编号:     中图分类号:    文献标志码:
基金项目:云南省科技人才和平台计划,编号2019HB081.
引用文本:
翟忠标,牟兴兵,陈景.锡渣还原氯化焙烧--磁选回收有价金属试验[J].矿冶,2020,(4):.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号