中文摘要: 针对云锡铜业高砷高锡低铜白烟尘,开展酸化焙烧选择性脱砷的研究,考察活性炭配比、浓硫酸配比、焙烧温度、焙烧时间对砷、锡、铅、锌、铋、铜挥发率的影响。在焙烧温度450 ℃、焙烧时间3 h、活性炭加入量5%、硫酸加入量30%较优条件下,白烟尘砷挥发率为94.28%,锡、铅、锌、铋、铜挥发率分别为2.34%、3.71%、2.96%、1.43%、1.64%。酸化焙烧实现了砷的选择性挥发,使白烟尘中的砷形成开路,为后续有价金属的分别回收创造了有利条件。
Abstract:Aiming at the high arsenic, high tin, low copper white smoke and dust of the Yuntin Copper Industry, a study on the selective arsenic removal of acidification roasting was carried out, and the ratio of activated carbon, concentrated sulfuric acid, roasting temperature, and roasting time were investigated for the effects of arsenic, tin, lead, zinc, and bismuth. , The influence of copper volatilization rate. Under the optimal conditions of calcination temperature 450 ℃, calcination time 3 h, activated carbon addition 5%, sulfuric acid addition 30%, the white smoke dust arsenic volatilization rate is 94.28%, tin, lead, zinc, bismuth, and copper volatilization rate is 2.34 respectively %, 3.71%, 2.96%, 1.43%, 1.64%. The acidification roasting realizes the selective volatilization of arsenic, which opens the arsenic in the white smoke and creates favorable conditions for the subsequent recovery of valuable metals.
文章编号:20211019001 中图分类号: 文献标志码:
基金项目:
作者 | 单位 | |
刘会讲 | 云南锡业研究院有限公司 | kazy2004@163.com |
季登会* | 云南锡业研究院有限公司 | 280845147@qq.com |
孙磊 | 云南锡业研究院有限公司 | 514983082@qq.com |
引用文本:
刘会讲,季登会,孙磊.铜冶炼白烟尘酸化焙烧工艺研究[J].矿冶,2022,31(2):.
刘会讲,季登会,孙磊.铜冶炼白烟尘酸化焙烧工艺研究[J].矿冶,2022,31(2):.