刚果(金)SICOMINES铜钴矿浮-磁工艺优化研究
范海宝, 高丹校, 王顺, 李勇, 张自旭
(华刚矿业股份有限公司)
Optimization of float-magnetic process of Sicomines copper-cobalt ore in the DRC
Fan Haibao, Gao Danxiao, Wang Shun, Li Yong, Zhang Zixu
(Huagang Mining Co. Ltd.)
摘要
图/表
参考文献
相似文献
本文已被:浏览 1253次   下载 732
投稿时间:2023-05-16    修订日期:2023-06-02
中文摘要: 刚果(金)SICOMINES铜钴矿属于高氧化率难选铜钴矿,使用浮选-磁选联合工艺处理该矿石,其磁选精矿品位低,产率较大,磁选精矿直接浸出经济效益差。为提高该铜钴矿磁选精矿铜钴选冶综合效益,对磁选精矿进行再磨再选处理,采用硫氢化钠作为硫化剂,黄药作为捕收剂,2#油作为起泡剂,进行了磁选精矿再磨再选试验研究,在最佳条件下,可获得产率18.48%、铜品位3.84%、钴品位0.36%、铜回收率56.15%、钴回收率35.20%的精矿,且精矿铜浸出率可达到85.64%,钴的浸出率可达到74.05%,吨铜净酸耗为2.15t/t铜,获得较好的经济效益。
Abstract:In order to improve the recovery rate of copper and cobalt in the magnetic separation concentrate of Congo (Kinshasa) SICOMINES Copper-Cobalt mine , in view of the low copper-cobalt grade in the magnetic separation concentrate and the poor enrichment effect of magnetic separation. In order to improve the comprehensive benefits of copper-cobalt ore magnetic separation concentrate copper-cobalt metallurgy, the magnetic separation concentrate was remilled and re-selected, sodium hydrosulfide was used as vulcanizing agent, yellow medicine as collector, 2# oil as foaming agent, magnetic separation concentrate regrinding and re-selection test research was carried out, under the best conditions, concentrate with yield of 18.48%, copper grade of 3.84%, cobalt grade of 0.36%, copper recovery rate of 56.15%, cobalt recovery rate of 35.20%, and the copper leaching rate of concentrate can reach 85.64%. The leaching rate of cobalt can reach 74.05%, and the net acid consumption of copper per ton is 2.15t/t copper, which obtains good economic benefits.
文章编号:20230516002     中图分类号:TD952    文献标志码:
基金项目:
引用文本:
范海宝,高丹校,王顺,李勇,张自旭.刚果(金)SICOMINES铜钴矿浮-磁工艺优化研究[J].矿冶,2023,32(6):.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号