铜钴氧化矿硫酸浸出过程优化
杨要峰
(迪兹瓦矿业股份有限公司)
Optimization of sulfuric acid leaching process of copper-cobalt oxide ore
YANG Yao-feng
(DEZIWA Mining Company)
摘要
图/表
参考文献
相似文献
本文已被:浏览 348次   下载 268
投稿时间:2023-08-01    修订日期:2023-08-02
中文摘要: 针对低品位氧化铜钴矿硫酸体系铜、钴浸出过程,考察了矿石粒度、浸出酸量、SO2用量、液固比、浸出时间对Cu、Co及杂质Fe、Mn、Si的浸出影响规律。并进一步对单因素强化浸出措施进行了经济性分析,最终确定了较优的浸出控制条件,磨矿时间5 min、pH值~1.5、SO2量6.37 kg?t-矿-1、液固比3:1(mL/g),浸出时间5小时。在该条件下,Cu、Co的浸出率分别为93.67%和75.90%,Mn的浸出率约为87.00%,Fe和Si的浸出率分别为2.66%和0.24%。
中文关键词:     硫酸浸出  氧化矿
Abstract:The effects of ore size, acid dosage, SO2 dosage, liquid-solid ratio and leaching time on the leaching efficiency of Cu, Co and impurities Fe, Mn and Si were investigated during the sulfuric acid leaching process of copper-cobalt oxide ore. Furthermore, the economic benefits of single factor enhanced leaching were analyzed. The optimal leaching control conditions were determined, including grinding time of 5 min, pH value of about 1.5, SO2 dosage of 6.37 kg/ t-ore, liquid-solid ratio of 3:1 (mL/g), leaching time of 5 hours. Under these conditions, the leaching efficiency of Cu and Co were 93.67% and 75.90% respectively, Mn was about 87.00%, and Fe and Si were 2.66% and 0.24% respectively.
文章编号:20230801001     中图分类号:    文献标志码:
基金项目:国家重点研发计划:铜再生灰多组分可控相变-梯级分离提取技术与示范(2019YFC1908404)
引用文本:
杨要峰.铜钴氧化矿硫酸浸出过程优化[J].矿冶,2023,32(5):.

为了给您提供更优质的网页浏览体验,请使用 Firefox 、Chrome、IE10、IE11、360极速模式、搜狗极速模式、QQ极速模式等浏览器,其他浏览器不建议使用

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299751

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299751

传真:010-63299754

QQ:XXXXXXX

Email:kuangye@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼905 北京矿冶研究总院《矿冶》编辑部

关注微信公众号